We try for excellence, service the customers", hopes to be the most effective cooperation workforce and dominator company for staff, suppliers and shoppers, realizes price share and ongoing marketing for Compound Plastic, Engineering Plastics Additives, Anti Scratches Funtional Additive, Excellent quality, competitive prices, prompt delivery and dependable service are guaranteed Kindly let us know your quantity requirement under each size category so that we can inform you accordingly.

China Wholesale High Temperature Slip Masterbatch Factories – ANTI-WEAR AGENT NM-3C – Silike Detail:

Anti-abrasion masterbatch NM-3C is a pelletized formulation with 50% active ingredient dispersed in rubber . It’s particularly developed for rubber shoe’s sole compounds, helps to improving the final items abrasion resistance and decrease the abrasion value in the thermoplastics .

Compare to conventional lower molecular weight Silicone / Siloxane additives,like Silicone oil, silicone fluids or other type abrasion additives, SILIKE Anti-abrasion Masterbatch NM-3C is expected to give a much better abrasion resistance property without any influence on hardness and color.

Grade	NM-3C
Appearance	White pellet
active ingredients content %	50
Carrier	rubber
Melt index ( 190℃, 10.00KG ) g/10min	5.10 ( typical value )
Dosage % (w/w)	0.5～5%

(1) Improved abrasion resistance with decreased abrasion value

(2) Impart the processing performance and final items appearance

(3) Eco-friendly

(4) No influence on hardness and color

(5) Effective for DIN, ASTM, NBS , AKRON, SATRA, GB abrasion tests
…..

Applicable for NR, NBR, EPDM, CR, BR, SBR, IR, HR, CSM, etc.

Basic formula	NR/NBR	40	+NM-3C	0	2%	4%	6%
	Engine oil	5	DIN value	170	139	129	117
	CB	50

Mix NM-3C with rubber into internal mixer during the temperature rising mixture process, to evenly mix. The output temperature should be above 100 ℃. NM-3C is recommend to be used with Si-69.

When added to rubber at 0.2 to 1% , improved processing and flow of the resin is expected, including better mold filling, less extruder torque, internal lubricants, mold release and faster throughput; At a higher addition level , 2~10%, improved surface properties are expected, including lubricity , slip, lower coefficient of friction and greater mar/scratch and abrasion resistance

25Kg / bag , craft paper bag

Transport as non-hazardous chemical. Store in a cool , well ventilated place .

Original characteristics remain intact for 24 months from the production date , if kept in recommend storage.

Chengdu Silike Technology Co., Ltd is a manufacturer and supplier of silicone material, who has dedicated to R&D of the combination of Silicone with thermoplastics for 20⁺ years, products including but not limited to Silicone masterbatch , Silicone powder, Anti-scratch masterbatch, Super-slip Masterbatch, Anti-abrasion masterbatch, Anti-Squeaking masterbatch, Silicone wax and Silicone-Thermoplastic Vulcanizate(Si-TPV), for more details and test data, please feel free to contact Ms.Amy Wang Email: amy.wang@silike.cn