Si-TPV design your silky touch and stain resistance smart wearable devices,
excellent dirt collection resistance, silky and skin-friendly touch,
SILIKE Si-TPV® 2150-55A thermoplastic elastomer is a patented dynamic vulcanized thermoplastic silicone-based elastomer which made by a special compatible technology to help silicone rubber dispersed in TPO evenly as a 2~3 micron particles under microscope. Those unique materials combine the strength, toughness and abrasion resistance of any thermoplastic elastomer with desirable properties of silicone: softness, silky feel, UV light and chemicals resistance which can be recycled and reused in traditional manufacturing processes.
Si-TPV® 2150-55A can excellent bond to TPE and similar polar substrates like PP, PA, PE, PS, etc… It is a product developed for soft touch overmolding on wearable electronics, accessory cases for electronic devices, automotive, high-end TPE, TPE wire industries ……
Test item | Property | Unit | Result |
ISO 37 | Elongation at Break | % | 590 |
ISO 37 | Tensile Streng | Mpa | 6.7 |
ISO 48-4 | Shore A Hardness | Shore A | 55 |
ISO1183 | Density | g/cm3 | 1.1 |
ISO 34-1 | Tear Strength | kN/m | 31 |
– | Modulus of Elasticity | Mpa | 4.32 |
– | MI( 190℃,10KG) | g/10 min | 13 |
– | Melt Temperature Optimum | ℃ | 220 |
– | Mold Temperature Optimum | ℃ | 25 |
Compatibility SEBS, PP, PE, PS, PET, PC, PMMA, PA
1. Provide the surface with Unique silky and skin-friendly touch, soft hand feeling with good mechanical properties.
2. Not contain plasticizer and softening oil, no bleeding / sticky risk, no odors.
3. UV stable and chemical resistance with excellent bonding to TPE and similar polar substrates.
4. Reduce dust adsorption, oil resistance and less pollute.
5. Easy to demould, and easy to handle.
6. Durable abrasion resistance & crush resistance & scratch resistance.
7. Excellent flexibility and kink resistance.
…..
Directly injection molding.
• Injection Molding Processing Guide
Drying Time |
2–4 hrs |
Drying Temperature |
60–80°C |
Feed Zone Temperature |
180–190°C |
Center Zone Temperature |
190–200°C |
Front Zone Temperature |
200–220°C |
Nozzle Temperature |
210–230°C |
Melt Temperature |
220°C |
Mold Temperature |
20–40°C |
Injection Speed |
Med |
These process conditions may vary with individual equipment and processes.
• Secondary Processing
As a thermoplastic material, Si-TPV® material can be secondary processed for ordinary products.
• Injection Molding Pressure
The holding pressure largely depends on the geometry, thickness and gate location of the product. The holding pressure should be set to a low value at first, and then slowly increase until no related defects are seen in the injection molded product. Due to the elastic properties of the material, excessive holding pressure may cause serious deformation of the gate part of the product.
• Back pressure
It is recommended that the back pressure when the screw is retracted should be 0.7-1.4Mpa, which will not only ensure the uniformity of melt melting, but also ensure that the material is not severely degraded by shear. The recommended screw speed of Si-TPV® is 100-150rpm to ensure the complete melting and plasticization of the material without material degradation caused by shear heating.
1. Si-TPV elastomer products can be manufactured using standard thermoplastic manufacturing processes, including overmolding or co-molding with plastic substrates such as PP, PA.
2. The extremely silky feel of Si-TPV elastomer does not require additional processing or coating steps.
3. The process conditions may vary with individual equipment and processes.
4. A desiccant dehumidifying drying is recommended for all drying.
25KG / bag , craft paper bag with a PE inner bag
Transport as non-hazardous chemical. Store in a cool and well ventilated place.
Original characteristics remain intact for 12 months from the production date if kept in recommend storage.To help manufacturers of smart wearable devices solve the scratch or mar dirt collection easily problems, we developed a new stain-resistant grade of dynamic vulcanizate thermoplastic Silicone-based elastomers(Si-TPV) Eco-friendly material. Benefits for wearable devices, The surface of the Si-TPV®2150 series has the characteristics of smooth touch, good sweat and salt resistance, no stickiness after aging, and provides better scratch resistance and wear resistance. The Si-TPV®2150 series can be widely used in related application fields such as smart wearable devices, wires, digital electronic products, and clothing bags.