Slip Silicone Masterbatch SF105D For BOPP/CPP Blown Films

SF105D is an innovated smooth masterbatch specially developed and produced for BOPP/CPP film products. With specially modified poly dimethyl siloxane as the active ingredient, this product overcomes the key defects of general slip additives, including the slip agent continuous precipitation from the surface of the film, the smooth performance will decrease with time goes by and temperature increasing, odor, etc.

SF105D slip masterbatch is suitable for BOPP/CPP film blowing molding, casting molding, processing performance is the same as the base material, no need to change.

Process conditions: widely used in the production of BOPP/CPP blowing film, casting film and extrusion coating and so on.

Send email to us

Product Detail

Product Tags

Sample service

Description

SF105D slip masterbatch is suitable for BOPP/CPP film blowing molding, casting molding, processing performance is the same as the base material, no need to change.

Process conditions: widely used in the production of BOPP/CPP blowing film, casting film and extrusion coating and so on.

Product Specifications

Grade	SF105D
Appearance	white pellet
MI (230℃,2.16Kg) (g/10min)	4~15
Surface density（Kg/cm³）	500~600
Volatile content (%)	≤0.2

Benefits

1. SF105D is used for high speed packaging cigarette film which needs to have good hot and smooth performance on metal.

2. When SF105D film is added, the friction coefficient has little effect with temperature. High temperature hot smooth effect is good.

3. in the process of processing will not precipitate, will not produce white cream, prolong the cleaning cycle of equipment.

4. The maximum addition amount of SF105D in the film is 10% (generally 2~10%), and the higher the addition amount will affect the transparency of the film. The larger the amount, the thicker the film, the greater the effect of transparency.

5. SF105D contains organic anti-blocking agent, can add less or no anti-blocking agent.

6. If needs antistatic performance, could add antistatic masterbatch.

Application advantages

Surface performance: no precipitation, reduce the film surface friction coefficient, improve the surface smoothness;

Processing performance: good processing lubricity, improve processing efficiency.

How to use

· SF105D slip masterbatch is used for BOPP/CPP film blowing molding and casting molding and the processing performance is same as the base material, no need to change.

· Dosage is generally 2~ 10%, and can make proper adjustments according to the product characteristics of raw materials and the thickness of the production films.

· During production, add the SF105D slip masterbatch directly to the substrate materials, mixed evenly and then added into the extruder.